An experimental technique for measuring the average interdislocation internal stress in crystals is described and measurements for LiF single crystals undergoing high temperature sigmoidal creep are reported. Quantitative predictions of the magnitude of the average internal stress are made using Haasen's treatment of sigmoidal creep and are compared with the measured internal stresses. The comparison shows the theory and experiment to be in good agreement. CONTRAINTES INTERNES MOYENNES DANS LES MONOCRISTAUX DE LiF AU COURS DU FLUAGE A HAUTE TEMPERATURE Les auteurs decrivent une technique experimentale de mesure de la contrainte interne moyenne interdislocations dans les cristaux et presentent des mesures pour des monocristaux de LiF soumis a un fluage signofdal a haute temperature. Des previsions quantitatives de l'amplitude de la contrainte interne moyenne sont obtenues en utilisant la theorie de Haasen du fluage sigmoidal, et ces valeurs sont comparees aux contraintes internes mesurees. La comparaison montre qu'il existe un bon accord entre la theorie et l'experience. MITTELWERTE DER INNEREN SPANNUNGEN IN LiF-EINKRISTALLEN WAHREND DES HOCHTEMPERATURKRIECHENS Ein experimentelles Verfahren zur Messung von Mittlewerten der inneren Spannungen zwischen Versetzungen wird beschrieben und auf LiF-Einkristalle wahrend des sigmoidalen Kriechens bei hohen Temperaturen angewandt. Unter Anwendung von Haasens Behandlung des sigmoidalen Kriechens werden quantitative Vorhersagen dsr GroDe der mittleren inneren Spannungen gemacht und mit gemessenen inneren Spannungen verglichen. Der Vergleich zeigt gute Ubereinstimmung zwischen Theorie und Experiment,. * It is clear that ii/r and di/u may be used interchangeably since all of the crystals used in this experiment are tested in the same orientation ((001)).