The short range order and size effect coefficients as well as the thermal and static atomic displacements h&ve been measured in b.c.c. solid solutions of titanium-molybdenum using X-ray diffraction techniques. These solutions exhibit a strong preference for unlike near-neighbors even though a superlattice was not found. The size effect coefficients for the first shell of atoms were negative, indicating that the molybdenum atoms were smaller than the titanium atoms in solution.
Center-to-center distances bet,ween the different pairs of nearest neighbor atoms were calculated from the size effect coefficients and the lattice parameters. Ti-Ti and MO-MO distances tended to approach the average distance in the solution at compositions between 20 and 50 at.% molybdenum. At 75 per cent molybdenum the NO-MO distance was smaller than in pure molybdenum and this was taken to indicate an electron exchange in the sohltion. ARRANGEMENT D'ATOMES DANS LES SOLUTIONS SOLIDES DE TITANE MOLYBDENE L'ordre zt courte distance et des coefficients d'effet de dimension einsi que les dbplacements atomiques thermiques et statiques ont 6tB mesur& dans des solutions solides de titane molybdbne de reseau cubique cent& par diffraction de rayons X. Les solutions montrent une grande pr&f&ence pour leurs voisins non semblables, quoiqu'une surstructure n'a pas pu &re trouv8e. Les coefficients d'effet de dimension pour les atomes de la premihre orbite Btaient &g&ifs, co qui indique que les atomes de molybd8ne Btaient plus petits que les atomes de titan0 en solution. Les distances d'un centre iL l'autre entre deux paires diffbrentes d'atomes les plus rapprochbs ant BtB c&x&es d'aprbs le coefficient d'effet ou dimension et d'ap&s les param&res du rkseau. Les distances Ti-Ti et MO-MO tendent iL s'approcher de la distance moyenne dans la solution pour des teneurs entre 20 et 50% atomiques de molybdhne. Pour une teneur de 75% de molybdBne la distance Mo-Mo Qtait plus petite que celle dans le molybdene pur, ce qui indiquerait un &change d'6lectrons dans la solution. ATOMANORDNUNGEN IN FESTEN LiiSUNGEN AUS TITAN UND MOLYBDliN RGntgenographisch wurden die Nahordnungs-und GrBssaneffekt-Koeffizienten und die therm&hen und statistischen Atomverschiebungen in k.r.z. festen Liisungen aus Titan und Molybdiin bestinunt. Diese Liisungen zeigen ein starkes Vorherrschen van ungleichen niichsten Nachbarn, obwohl keine tiberstruktur gefunden wurde. Die GrGsseneffekt-Koeffizienten der Atome erster Schale waren negativ; des weist darauf hin, dass die Molybdiinatome in der Liisung kleiner sind als die Titanatome. Die Mittelpunktsabstiinde zwischen verschiedenen Paaren niichstbenachbarter Atome wurden &us den Griisseneffekt-Koeffizienten und den Gitterparametern berechnet. Ti-Ti und M+Mo Abstiinde nlihern sich zwischen 20 und 50 At% Molybdiin dem durchschnittlichen Atomabstand in der LGsung an. Bei 75 At% MolybdBn ist der Mo-Mo-Abstand kleiner 81s in reinen Molybdiin, dies wurde alsAnzeichen eines Elektronenaustauschs in der LGsung gedeutet.