Atmospheric corrosion of ordinary mild steel in the Arabian Gulf environment

✍ Scribed by Dr. Emad Taqi; Dr. H. Al Madani; Dr. E. Shaji

Publisher
John Wiley and Sons
Year
1993
Tongue
German
Weight
895 KB
Volume
44
Category
Article
ISSN
0947-5117

No coin nor oath required. For personal study only.

✦ Synopsis

Abstract

Atmospheric corrosion tests were carried out on mild steel to study its corrosion behaviour in the Arabian Gulf environment. Results of exposure tests indicate that the atmospheric attack proceeds in a paralinear fashion during the first year of exposure. S.E.M. examination of the oxide scale showed extensive porosity, spallation and cracking with the appearance of platelike structures close to pitted sites. X‐ray diffraction analysis revealed the presence of γFeOOH, αFeOOH, αFe~2~O~3~ and Fe~3~O~4~. EDX analysis disclosed that specimen surface contaminants are primarily constituents of sea spray.

📜 SIMILAR VOLUMES

Performance of Cu and Cu-Zn alloy in the
Performance of Cu and Cu-Zn alloy in the Arabian Gulf environment
✍ H. Saricimen; A. Quddus; A. Ahmad; A. Aksakal; T. A. Siddique; A. Ul-Hamid 📂 Article 📅 2010 🏛 John Wiley and Sons 🌐 German ⚖ 551 KB

## Abstract Corrosion performance of copper and brass coupons during 15 month exposure in atmosphere, underground and splash zone conditions was undertaken at Khaleej Mardumah test site located in the industrial/coastal city of Jubail along the Arabian Gulf coast, Saudi Arabia. The environmental in

Performance of austenitic stainless stee
Performance of austenitic stainless steels in MSF desalination plant flash chambers in the arabian gulf
✍ H. Saricimen; M. Shamim; I.M. Allam; M. Maslehuddin 📂 Article 📅 1990 🏛 Elsevier Science 🌐 English ⚖ 725 KB

The corrosion behavior of AISI type 304L (304L (304L SS) and 316L (316L SS) stainless steels in a multi-stage flash (MSF) desalination plant located on the Arabian Gulf coast was investigated . The 304L and 316L stainless steel liner plates in the flash chambers of the plant developed severe localiz

Hydrogen permeation behavior and corrosi
Hydrogen permeation behavior and corrosion monitoring of steel in cyclic wet–dry atmospheric environment
✍ C. Zheng; Y. Huang; C. Huo; Q. Yu 📂 Article 📅 2007 🏛 John Wiley and Sons 🌐 German ⚖ 190 KB

## Abstract Hydrogen permeation of 16Mn steel under a cyclic wet–dry condition was investigated by Devanathan–Stachurski's electrolytic cell with a membrane covered on the exit side by a nickel layer and the weight loss was measured for each wet–dry cycle. The results show that hydrogen permeation

Atmospheric corrosion of aluminium in th
Atmospheric corrosion of aluminium in the northern Taklamakan Desert environment
✍ S. Sun; Q. Zheng; J. Wen; D. Li 📂 Article 📅 2009 🏛 John Wiley and Sons 🌐 German ⚖ 746 KB

## Abstract Atmospheric corrosion of aluminium in the northern Taklamakan Desert environment in China was investigated through the field exposure over a period of 2 years and the laboratory‐accelerated test of dry‐wet cycles. The results demonstrated that aluminium 1050 suffered serious atmospheric

Atmospheric corrosion of galvanized stee
Atmospheric corrosion of galvanized steel and aluminium in marine and marine-industrial environments of Saudi Arabia
✍ A. I. Almarshad; S. Syed 📂 Article 📅 2008 🏛 John Wiley and Sons 🌐 German ⚖ 122 KB

## Abstract Three‐year exposure programme was carried out in Saudi Arabia at nine test stations with different climatic and pollution conditions. The aim of this study was to evaluate the joint effect of atmospheric pollutants (Cl^−^ and SO~2~), relative humidity (RH) and temperature (T) on the atm

Electrochemistry and XPS study of an imi
Electrochemistry and XPS study of an imidazoline as corrosion inhibitor of mild steel in an acidic environment
✍ O. Olivares-Xometl; N. V. Likhanova; R. Martínez-Palou; M. A. Domínguez-Aguilar 📂 Article 📅 2009 🏛 John Wiley and Sons 🌐 German ⚖ 388 KB

## Abstract The effect of 2‐(2‐heptadec‐8‐enyl‐4,5‐dihydro‐imidazol‐1‐yl)‐ethylamine on the corrosion behavior of mild steel in aqueous hydrochloric acid was investigated using weight loss measurements, polarization scans, electrochemical impedance, and X‐ray photoelectron spectroscopy (XPS). The i