Rocksalt crystals were irradiated with X-rays.
The so produced surface hardening and the resoftening due to annealing at different temperatures were followed. The activation energy of the process associated with the annealing in the temperature range 150"-300Β°C was derived. In agreement with experimental results obtained by other workers, we find it likely to assume that clusters of point defects are the principal cause of the surface hardening.
For annealing temperatures below 300Β°C the resoftening would mainly result from the growth in size of these aggregates, and their corresponding decrease in number.
RECUIT
DU DURCISSEMENT DE SURFACE INDUIT PAR LES RAYONS X DANS DES CRISTAUX NaCl Les cristaux de NaCl ont BtB irradibs B l'aide de rayons X. Le durcissement de surface ainsi obtenu et la restauration due au recuit & des temperatures diff&entes a 8tB BtudiBe. L'Bnergie d'activation lors du recuit dans la gamme de temperatures entre 150 et 300Β°C a BtB dbterminbe. En accord avec les r&ultats experimentaux obtenus par d'autres chercheurs, nous trouvons que les segregations de dbfauts ponctuels sont la cause principale du durcissement de surface.
Pour des tempi?ratures de recuit sous 3OO"C, la restauration r&s&e principalement de la croissance des dimensions de ces agrbgats et de la d&xoissance de leur nombre.