Anisotropic ionic conductivity of lithium-doped sulfonated PBI

✍ Scribed by R. J. Spry; M. D. Alexander Jr.; S. J. Bai; T. D. Dang; G. E. Price; D. R. Dean; B. Kumar; J. S. Solomon; F. E. Arnold

• Publisher: John Wiley and Sons
• Year: 1997
• Tongue: English
• Weight: 271 KB
• Volume: 35
• Category: Article
• ISSN: 0887-6266
• DOI: 10.1002/(sici)1099-0488(199712)35:17<2925::aid-polb15>3.0.co;2-9

✦ Synopsis

The conductivity study results of lithium-doped sulfonated PBI, a conjugated rigid rod polymer, poly [(1,7-dihydrobenzo[1,2-d:4,5-d ]

derivatized with pendants of propane sulfonate Li / ionomer are reported. The room-temperature DC four-probe conductivity parallel to the surface of cast films was as large as 8.3 1 10 03 S/cm. Similar measurements with an eightprobe configuration showed no difference between bulk and surface conductivity. The ionic nature of the conductivity was indicated by constant voltage depletion experiments and by secondary ion mass spectroscopy measurements of the residues near the electrodes. The DC two-probe conductivity measured transverse to the sample surface was three to four orders of magnitude smaller than longitudinal conductivity, while the AC two-probe conductivity was even less. Electron microscopy indicated that the films had a layered structure parallel to the surfaces. This structural anisotropy was confirmed by refractive index values obtained from wave-guide experiments and by wide angle X-ray scattering.