In high purity magnesium, the internal friction spectra are composed of several peaks which have been identified. They are similar to the ones observed in f.c.c. metals. We distinguish; the rr, peak at I5 K, the Bordoni peaks B, and B2 at 40 and 80 K, the Hasiguti peaks P, and P2 at 105 and 220 K and the Pa peak at 420 K. The primary and secondary features of the Bordoni peaks are studied. The obtained results are consistent with the relaxation model of double-kink nucleation. In particular, important non-linear effects are observed after cold-work. The others manifestations are briefly discussed. The internal friction spectra are very sensitive to the presence of impurities. In lees pure magnesium, it is more difficult to recognize the preceding relaxation peaks: the internal friction background is higher and a large maximum due to the impurities breakaway appears.
R&sum&-Dans un magnesium de haute purete, le spectre de fottement interieur est compose de plusieurs pits qui ont Cti identifies. Ces pits sont semblables a ceux observis dans Ie metaux c.f.c. II apparait ainsi: le pit A, a I5 K, les pits de Bordoni Et et ffs a 40 et 80 K, les pies de Hasiguti P, et P2 B I05 et 220 K et le pit P, g 420 K. Les proptiitcS prima&s et secondaires de la relaxation de Bordoni ont CtC itudi6es. D'importants effets non lin&aires sont obser&. Les t%ultats obtenus sont tout-a-fait en accord avec le modele de relaxation due B la formation des doubles dCcrochements. Les autres manifestations sont egalement bri&vement discart&. Les spectres de frottement inttrieur sont t&s sensibles A la put&. Dam un magnesium moins pur, il est plus di5%le de reconnaitre les pits precedents: Ie fond continu de frottement interieur e-st plus tleve et il aparait un large maximum dti au d&sancrage des impuretis. Zusanunenfasatmg-Die Spektren der inneren Reibung bestehen bei hochreinem Magnesium aus verschiedenen. schon identitixierten Maxima. Sic ihneln denen der kfz. Metalle: das a,-Maximum bei I5 K, die Bordoni-Maxima B, turd B2 bci 40 und 80 K, die Hasiguti-Maxima P, und P2 bci 105 und 220 K und das Pa-Maximum bei 420 K. Die prim&en und sekundliren Eigenschaften der Bordoni-Maxima werden untersucht. Die erhaltenen Ergebnisse sind vertriiglich mit dem Relaxationsmodell der Bildung von Doppelkinken. Insbesondere werden wichtige nichtlineare Effekte nach Verfomtung beobachtet. Andere Beobachtungen werden kurz diskutiert. Die Spektren der inneren Reibung hiingen sehr empfindlich von vorhandenen Verunreinigungen ab. In weniger reinem Magnesium sind die vorher e-ten Maxima schwer xu erkennen: der Untergrund der inneren Reibung ist hiiher und ein go&s Maximum erscheint, welches vom LosreiBen von den Verunreinigungen herrtihrt.