Analysis of photopolymerization behavior of UDMA/TEGDMA resin mixture and its composite by differential scanning calorimetry

✍ Scribed by Yasuhiro Tanimoto; Tohru Hayakawa; Kimiya Nemoto

• Publisher: John Wiley and Sons
• Year: 2005
• Tongue: English
• Weight: 183 KB
• Volume: 72B
• Category: Article
• ISSN: 1552-4973
• DOI: 10.1002/jbm.b.30151

✦ Synopsis

Abstract

The aim of this study was to investigate the extent of polymerization (Ep) in terms of polymerization rate of UDMA/TEGDMA resin mixtures and its composite resin, by using a differential scanning calorimeter (DSC) technique employing a photopolymerization apparatus. The resin mixtures used in this study consisted of urethane dimethacrylate (UDMA) as a base monomer and triethyleneglycol dimethacrylate (TEGDMA) as a low viscosity monomer. The concentration of TEGDMA in the mixed monomer was varied to 0, 20, 40, 60, 80, and 100 mol %. Additionally, using a base monomer consisting of 60 mol % UDMA and 40 mol % TEGDMA, four kinds of composites with silica filler of 0, 20, 40, 60, and 70 wt %, were prepared in this study. The general reaction profile and Ep values were obtained from the DSC curves. Increasing the concentration of TEGDMA resulted in a decrease in the viscosity of the UDMA/TEGDMA mixture, a delay in the time to maximum polymerization rate, and an increase in the Ep values of the resin mixtures. Furthermore, Ep values decreased with increasing filler content between 0 and 60 wt % but did not decrease further between 60 and 70 wt %. © 2004 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 72B: 310–315, 2005