Analysis of creep curves of a nickel base superalloy in a wide stress/temperature range

โœ Scribed by M. Maldini; G. Angella; V. Lupinc

Publisher
Elsevier Science
Year
2007
Tongue
English
Weight
350 KB
Volume
462
Category
Article
ISSN
0921-5093

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Microstructure of a nickel-base superall
Microstructure of a nickel-base superalloy after creep in [011] orientation at 1173 K
โœ Thomas Kuttner; Monika Feller-Kniepmeier ๐Ÿ“‚ Article ๐Ÿ“… 1994 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 718 KB

Tensile creep tests in the [011] direction have been performed on two specimens of SRR99 at 1173 K under a load of 300 MPa. The microstructure was analysed by transmission electron microscopy investigations after plastic strains of 0.1% and 0.29%. At both strains, the 7' phase is not sheared by disl

In situ measurement of the lattice param
In situ measurement of the lattice parameter mismatch of a nickel-base single-crystalline superalloy under variable stress
โœ A. Jacques; F. Diologent; P. Bastie ๐Ÿ“‚ Article ๐Ÿ“… 2004 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 109 KB

The evolution of the lattice parameters of the โฅ matrix and โฅ precipitates was measured in situ during high temperature tests of specimens with a raft microstructure at 1080 โ€ข C under variable load (0-300 MPa), done at the ESRF. Under low applied tensile stresses, the behavior of the specimens is pu