An AP-FIM study on metastable phases in AlAg binary alloy

✍ Scribed by K. Osamura; T. Nakamura; A. Kobayashi; T. Hashizume; T. Sakurai

• Publisher: Elsevier Science
• Year: 1986
• Weight: 903 KB
• Volume: 34
• Category: Article
• ISSN: 0001-6160
• DOI: 10.1016/0001-6160(86)90101-x

✦ Synopsis

The morphology and chemical composition of metastable phases in an Al-5.72 at.% Ag alloy have been investigated by means of atom-probe field ion microscopy. It was found that the n G.P. zones formed by aging at 413 K have an average solute concentration of 45.8 + 0.7 at.% Ag. the present data on zone size and interparticle distance were found to be consistent with data determined by small-angle X-ray scattering. When the specimen was aged at 436 K for 60 ks, both L G.P. zones and y' metastable phase were observed simultaneously. The solute concentration of t zones was determined to be 35.7 f 0.2 at.% Ag. They' phase was a plate-like precipitate lying on the { 111) matrix plane, and its solute concentration was 33.3 k 1.5 at.% Ag and its thickness was in the range of 2.3-7.0 nm. By combining the present data with other results certain pending questions on the structures of metastable phases in this alloy have been successfully solved.

Rkm~J+Nous avons CtudiC a l'aide de al sonde atomique de la sonde atomique de la microscopic ionique a effet de champ la morphologie et la composition chimique des phases metastables dans un alliage Al-5, 72 at.% Ag. Nous avons trouvi que les zones G.P. r7 qui se forment par vieillissement a 413 k ont une concentration en solute moyenne de 45,8 + 0,7 at.% Ag. Nos mesures de taille des zones et de distance interparticule sont coherentes avec les resultats obtenus par diffusion de rayons X aux petits angles. Lorsque l'bchatillon etait vieilli a 463 K pendant 60 ks, on observait simultanement des zones G.P. c et la phase mbtastable y '. Nous avon determine la concentration en solute des zones c a 35,7 5 0,2 at.% Ag. La phase y' se presentait sous la forme de plaquettes sit&es dans les plans { 11 I} de la matrice; sa concentration en solute btait de 33,3 + 1,5 at.% Ag et son bpaisseur etait comprise entre 2,3 et 7,0 nm. En combinant nos resultats avec des resultats anterieurs, nous avons pu resoudre avec succts un certain nombre de questions ouvertes sur la structure des phases metastables dans cet alliage.