Amorphous and nanocrystalline titanium nitride and carbonitride materials obtained by solution phase ammonolysis of Ti(NMe2)4
✍ Scribed by Andrew W. Jackson; Olga Shebanova; Andrew L. Hector; Paul F. McMillan
- Publisher
- Elsevier Science
- Year
- 2006
- Tongue
- English
- Weight
- 427 KB
- Volume
- 179
- Category
- Article
- ISSN
- 0022-4596
No coin nor oath required. For personal study only.
✦ Synopsis
Solution phase reactions between tetrakisdimethylamidotitanium (Ti(NMe 2 ) 4 ) and ammonia yield precipitates with composition TiC 0.5 N 1.1 H 2.3 . Thermogravimetric analysis (TGA) indicates that decomposition of these precursor materials proceeds in two steps to yield rocksalt-structured TiN or Ti(C,N), depending upon the gas atmosphere. Heating to above 700 1C in NH 3 yields nearly stoichiometric TiN. However, heating in N 2 atmosphere leads to isostructural carbonitrides, approximately TiC 0.2 N 0.8 in composition. The particle sizes of these materials range between 4-12 nm. Heating to a temperature that corresponds to the intermediate plateau in the TGA curve (450 1C) results in a black powder that is X-ray amorphous and is electrically conducting. The bulk chemical composition of this material is found to be TiC 0.22 N 1.01 H 0.07 , or Ti 3 (C 0.17 N 0.78 H 0.05 ) 3.96 , close to Ti 3 (C,N) 4 . Previous workers have suggested that the intermediate compound was an amorphous form of Ti 3 N 4 . TEM investigation of the material indicates the presence of nanocrystalline regions o5 nm in dimension embedded in an amorphous matrix. Raman and IR reflectance data indicate some structural similarity with the rocksalt-structured TiN and Ti(C,N) phases, but with disorder and substantial vacancies or other defects. XAS indicates that the local structure of the amorphous solid is based on the rocksalt structure, but with a large proportion of vacancies on both the cation (Ti) and anion (C,N) sites. The first shell Ti coordination is approximately 4.5 and the second-shell coordination $5.5 compared with expected values of 6 and 12, respectively, for the ideal rocksalt structure. The material is thus approximately 50% less dense than known Ti x (C,N) y crystalline phases.