Ambiguous Effect of cathodic polarization on crack growth as the general regularity of stress-corrosion cracking of structural materials

An ambiguity of the cathodic polarizatio

An ambiguity of the cathodic polarization effect on crack growth during stress corrosion cracking of aluminum alloys

✍ V. A. Marichev 📂 Article 📅 1983 🏛 John Wiley and Sons 🌐 German ⚖ 652 KB

## Abstract The kinetics of crack growth under the conditions of stress corrosion cracking of aluminum alloys in electrolytes with different anion composition and pH values from 0 to 13 has been studied. It is shown that for the majority of alloy‐electrolyte systems anodic polarization accelerates