Acidity and catalytic activity of mesoporous ZSM-5 in comparison with zeolite ZSM-5, Al-MCM-41 and silica–alumina

✍ Scribed by K. Suzuki; Y. Aoyagi; N. Katada; M. Choi; R. Ryoo; M. Niwa

• Publisher: Elsevier Science
• Year: 2008
• Tongue: English
• Weight: 821 KB
• Volume: 132
• Category: Article
• ISSN: 0920-5861
• DOI: 10.1016/j.cattod.2007.12.010

✦ Synopsis

Acidity of mesoporous HZSM-5 prepared using amphiphilic organosilane template molecules was measured. Brønsted acid sites were observed in the prepared sample, and the number and the strength of Brønsted acid sites were determined quantitatively by a method of infrared-mass spectroscopy/temperature-programmed desorption (IRMS-TPD) of ammonia. DH for ammonia adsorption as an index of the strength was ca. 150 kJ mol À1 that was almost the same as on usual HZSM-5, but the number was smaller than that of HZSM-5. From the measured acidity, it was concluded that the mesoporous materials contained a smaller concentration of Brønsted acid site notable on the structure of HZSM-5. Measurements of turnover frequency (TOF) in the catalytic cracking of octane supported the conclusion. Density functional calculations showed that the defect sites Al-OH and Si-OH attached to the Brønsted acid site changed the strength of the acid sites to show some possible structures of the weak and strong Brønsted acid sites included in the mesoporous HZSM-5. Acidities of Al-MCM-41 and silica-alumina were also measured, and the difference in the solid acidities of these materials was discussed.