✍ Scribed by A Hellström; O Vingsbo
No coin nor oath required. For personal study only.
quenched AI-Cu alloys are presented. They show that the density of helices and the amount of vacancies annihilated by the helices increase with increasing copper content. For equal quenching conditions the spread of diameter, pitch and slope of the helices is very large. Diameter, pitch and slope show no systematic variation with quench temperature or copper content. The mean slope of the helices is 1.7. ETUDE QUANTITATIVE EN MICROSCOPIE ELECTRONIQUE PAR TRANSMISSION DES DISLOCATIONS HELICOIDALES DANS DES ALLIAGES Al-Cu TREMPES On prbsente les r&ultats de mesures sur un grand nombre de dislocations h&licoidales dans des alliages d'aluminium et de cuivre trempbs. 11s montrent que la densite d'hblices et le taux de lacunes annihil&~s par les h&ices augmentant aveo la teneur en cuivre. La dispersion du diamhtre, du pas et de la pente des h&ices est t&s grande, pour des conditions de trempe identiques. Le diam&re, le pas et la pente des hblices ne pr&.entent pas de variations systbmatiques avec la temperature de trempe ou la teneur en cuivre. La pente moyenne des hblices est de 1,7. QUANTITATIVE ELEKTRONENMIKROSKOPISCHE UNTERSUCHUNG SPIRALFORMIGER VERSETZUNGEN IN ABGESCHRECKTEN AI-Cu-LEGIERUNGEN Es werden Messungen an einer Vielzahl von spiralfiirmigen Veraetzungen in Aluminium-Kupfer-Legierungen vorgelegt. Diese zeigen, daD die Dichte der Spiralversetzungen und die Anzahl der an ihnen ausgeheilten Leerstellen mit zunehmendem Kupfergehalt ansteigen. Bei vergleiohbaren Abschreckbedingungen ist die Spanne in Durchmesser, Ganghijhe und Steigung der Spiralversetzungen sehr gro13. Durchmesser, Ganghiihe und Steigung zeigen keine systematische Variation mit der Abschrecktemperatur und dem Kupfergehalt. Die mittlere Steigung der Spiralen ist 1,i'.
📜 SIMILAR VOLUMES