A New Solid Solution Series Linking LiTi2O4and Li2Ti3O7Ramsdellites: A Combined X-Ray and Neutron Study

✍ Scribed by Richard K.B. Gover; John T.S. Irvine

• Publisher: Elsevier Science
• Year: 1998
• Tongue: English
• Weight: 287 KB
• Volume: 141
• Category: Article
• ISSN: 0022-4596
• DOI: 10.1006/jssc.1998.7948

✦ Synopsis

We report the discovery of a new solid solution linking the LiTi 2 O 4 and Li 2 Ti 3 O 7 ramsdellite phases. The solid solution system is Li 1؉x Ti 2؊2x O 4 (04x40.143), where Li 2 Ti 3 O 7 can be written as Li 1.143 Ti 1.714 O 4 . Combined Rietveld refinement of Xray and neutron diffraction data sets has been used to determine the structure of various members of this solid solution. Unit-cell dimensions were seen to decrease as the Li content increased, in accord with the expected decrease in ionic size of Ti on oxidation. The Li channel and framework occupancy was seen to follow a simple substitutional mechanism; for every two titanium atoms in the framework that are replaced by lithium atoms, one lithium is lost from the channel sites, introducing a channel vacancy site. The lithium temperature factors were seen to increase over a composition range from x ‫؍‬ 0 to x ‫؍‬ 0.143. This is probably related to the increased number of channel vacancies. No evidence was observed for the splitting of the Li channel sites, even for the x ‫؍‬ 0.143 end member.