97/03142 High-density ceramics and their manufacture

Publisher
Elsevier Science
Year
1997
Weight
198 KB
Volume
38
Category
Article
ISSN
0140-6701

No coin nor oath required. For personal study only.

โœฆ Synopsis

The dry mixture that results from the blending of iron-rich oxide dust and other such wastes carbonaceous material is heated to release the volatiles with agglomeration. It is subsequently loaded into a preheated furnace with rotary hearth and heated for 5-12 min at 2150-2350ยฐF for smelting and discharging the metalized product suitable for recycling. The dry mixture is briquetted at >lO,OOO psi, and the briquettes are smelted at the nominal CO/CO: ratio of 2-5 for the reduction of metal oxides. The metalized Ferich briquettes are suitable for recycling to the steelmaking plant.

97103134

๐Ÿ“œ SIMILAR VOLUMES

97/03139 Ceramic cylindrical filters for
97/03139 Ceramic cylindrical filters for coal ash removal and their manufacture
๐Ÿ“‚ Article ๐Ÿ“… 1997 ๐Ÿ› Elsevier Science โš– 198 KB

The dry mixture that results from the blending of iron-rich oxide dust and other such wastes carbonaceous material is heated to release the volatiles with agglomeration. It is subsequently loaded into a preheated furnace with rotary hearth and heated for 5-12 min at 2150-2350ยฐF for smelting and disc

98/00652 Molded nitrogen oxide decomposi
98/00652 Molded nitrogen oxide decomposing ceramics and their manufacture
๐Ÿ“‚ Article ๐Ÿ“… 1998 ๐Ÿ› Elsevier Science โš– 205 KB

The paper investigates the sintering and crystallization behaviour of a LizO-AlsOs-Si02 glass powder containing TiOz and ZrOz. In-situ measuring methods of high-temperature dilatometry, high-temperature X-ray diffractometry and DTA at heating rates between 0.5 and 20 K/mm were conducted. By comparin